What kind of epoxy flooring material should be used to deal with terrazzo floor ash? The following is an introduction: At present, many factories have some problems because of the long use time of epoxy flooring material or the fact that the ground has not been treated. For example, the flooring material sand, the flooring material sand, the flooring material ash, the flooring material ash, and so on, the flooring material appears. Many pits, crusting of floor materials and many other problems: common cement concrete old ground, after several years of general use, under the action of forklift trucks, the ground will appear different degrees of ash, sand, shell, cracking, empty drum phenomenon. With the growth of service life, coupled with the role of carbonization, water erosion and weathering, the ground surface will continue to be powdered, affecting normal use.
水磨石地面主要表现在表面粗糙、不坚实，走动后表面有松散的水泥灰，用手摸时就掉干水泥面。随着多次走动会出现砂粒松动或有成片水泥硬壳剥落，这属于地面起沙，有的用小垂敲击地面时有空鼓声，在受重力后会出现开裂，这些都严重的破坏了地面的使用功能。 混凝土新地面及耐磨环氧地坪，出现不同程度的起灰、起砂、起壳、现象。 一切室内外的混凝土地坪（只要含有水泥）。均可硬化。
The terrazzo floor is mainly rough and unstable. After walking, there is loose cement paste on the surface. When touched by hand, the cement surface will be dried. Sand grains loosen or pieces of cement crust peel off as they move many times. This belongs to the sand-lifting of the ground. Some of them have empty drums when they hit the ground with a small pendulum and crack after being subjected to gravity, which seriously destroys the use function of the ground. New concrete floors and wear-resistant epoxy floors have different degrees of ash, sand, shell and phenomena. All indoor and outdoor concrete floors (as long as they contain cement). All can harden.
Apart from bleeding, lime, sand and peeling on terrazzo floor may also be caused by insufficient maintenance time or excessive loss of water. If the curing time is insufficient, it will cause a large amount of evaporation of water in the sun or dry air. The evaporation of surface water is faster than the bleeding speed of concrete, which will lead to a large amount of volatilization of surface water. Cement will slow down or even stop hydration. If surface cement is not fully hydrated, it will not be able to reach the design strength, establish sufficient surface strength, and then flour or rise. Quality problems such as sand and peeling.